OSTEEL also provides abrasion resistant steel plates and grinding balls.

Abrasion resistant plates are widely applied for machinary working in harsh envirements where good abrasion resistant and high strength performance are required.

OSTEEL adopts low alloy chemistry design and clean steel providing this kind of steel plates with high hardness, high strength, good toughness and weldability.

Applied Fields

The series of abrasion resistant steel plates are mainly applied for the machinery which are used in the industry of mining, construction, cement, port, power station and metallurgy,

such as scraper, bulldozer, excavator, loader, dump truck,cement mechanics,PCI devives, chute, crusher, grinder, mixer, filter, barge and etc..

The application of abrasion resistant steel plates prolongs the life expectancy and performance of the machinery, thus reduces the production cost.

Specification:

Grade	Delivery Conditions	Thckness/mm	Width/mm	Length/m
NM360	Q+T	5-70	1500-3200	≤20
NM400	Q+T	5-70	1500-3200	≤20
NM450	Q+T	5-70	1500-3200	≤20
NM500	Q+T	5-70	1500-3200	≤20
NM550	Q+T	5-70	1500-3200	≤20

Mechanical Properties

Grade	Brinell hardness	Y.S./MPa	T.S./Mpa	Elongation A50/%	Transverse charpy(-20℃)/J	Bending(90°)
NM360	330-390	≥900	≥1100	≥12	≥24	R=2a
NM400	380-440	≥950	≥1200	≥10	≥24	R=2.5a
NM450	420-480	≥1050	≥1300	≥9	≥24	R=3a
NM500	470-530	≥1150	≥1400	≥9	≥24	R=3.5a
NM550	520-580	≥1200	≥1450	≥7	≥20	R=4a

Remark:

1.R-bending radius,a-plate thckness;

2.Regarding mechanical properties shown in the table, apart from hardness, other technical indexes are negotiable.

3.During hardness testing, the surface of the sample should be milled by 1mm to 2.5mm, then the surface hardness will be tested.

Abrasion Resistant Tests
Impact abrasive test results.

weight loss with diferent abrasion time

Grade	Weight Loss /g				Relative Abrasion resistant
	30min	60min	90min	120min
NM500	0.12526	0.22445	0.33054	0.46865	6.15
NM450	0.22275	0.41841	0.59398	0.76194	3.78
NM400	0.28705	0.53435	0.75785	0.97632	2.95
Q345B	0.83532	1.57743	2.2334	2.88014	1

Test condition: impact energy 2J, grinding material 8-10 mesh quartz sand, flow rate 70g/h

Grinding ball

Grinding ball is one of the most widely used in industrial practice, the product is widely used in bearing steel ball, hardware, electronic, wrought iron, mechanical equipment, electric power, mining, metallurgy and other fields.